Thus , it can be stated that elevated temperature neutron irradiations can , in general , increase the frictional stress dus to interaction of mobile dislocations with some or all of the above mentioned defect clusters ( 1,2 ) .
Thus , it can be stated that elevated temperature neutron irradiations can , in general , increase the frictional stress dus to interaction of mobile dislocations with some or all of the above mentioned defect clusters ( 1,2 ) .
Seite
Most metals will show hardness increase after room - temperature irradiation ; however , high purity lead , aluminum , and magnesium do not . It is to be expected that hardness increases in other metals with low melting point would ...
Most metals will show hardness increase after room - temperature irradiation ; however , high purity lead , aluminum , and magnesium do not . It is to be expected that hardness increases in other metals with low melting point would ...