... Nomex 含量增加而逐漸上升,而 PU - Nomex 嵌狀共聚合體乃由於 PU 分子與 Nomex 分子鏈以共價鍵結合,故其熱性質具有較特殊、較高之單一玻璃轉位點及熔點。表二熱差分析儀測定之 Tg 、 Tm 值 Code Polymer Tg ( ° C ) Tm ( ° C ) PU PU 70 175 Nm Nomex 240 ...
... Nomex 含量增加而逐漸上升,而 PU - Nomex 嵌狀共聚合體乃由於 PU 分子與 Nomex 分子鏈以共價鍵結合,故其熱性質具有較特殊、較高之單一玻璃轉位點及熔點。表二熱差分析儀測定之 Tg 、 Tm 值 Code Polymer Tg ( ° C ) Tm ( ° C ) PU PU 70 175 Nm Nomex 240 ...
Seite 337
... Nomex 分子之 Tg 點過高(約 270 ~ 300 °C之間)超出本所動態粘彈儀所能測得範圍。由圖六( d )可知 PU / Nomex 摻合體其儲存係數( E )值與溫度變化關係,得知 Nomex 分子含量增大時,其儲存係數( E )值較高,可能因 PU 與 Nomex 分子依氫鍵結合,使摻合體產生微 ...
... Nomex 分子之 Tg 點過高(約 270 ~ 300 °C之間)超出本所動態粘彈儀所能測得範圍。由圖六( d )可知 PU / Nomex 摻合體其儲存係數( E )值與溫度變化關係,得知 Nomex 分子含量增大時,其儲存係數( E )值較高,可能因 PU 與 Nomex 分子依氫鍵結合,使摻合體產生微 ...
Seite 338
... Nomex 分子分散於 PU 聚合體基材內,就整體而言,由表面形態觀察可看出, PU 聚合體分子與 Nomex 呈兩相系統,在此情況下,因 Nomex 凝聚構造與 PU 基材之界面接著性低,既其相容性不佳,致其抗張強度反而下降。斷裂伸長率方面,則隨 Nomex 含量之增加而漸減,其因為 ...
... Nomex 分子分散於 PU 聚合體基材內,就整體而言,由表面形態觀察可看出, PU 聚合體分子與 Nomex 呈兩相系統,在此情況下,因 Nomex 凝聚構造與 PU 基材之界面接著性低,既其相容性不佳,致其抗張強度反而下降。斷裂伸長率方面,則隨 Nomex 含量之增加而漸減,其因為 ...
Andere Ausgaben - Alle anzeigen
Häufige Begriffe und Wortgruppen
academic departments access channels Admission to Higher Analysis appraisal costs bandwidth utilization base station blocking rate bolted joint C-test capture effect carbon fibers Citrobacter cloze College Entrance Examination colleges and universities Committee on Admission defectives density Development distribution Enterobacter Entrance Examination Committee equation even-numbered Executive Yuan expected error External Failure Costs grid groups Herbert higher education Improvement increase institutions of higher Internal failure Joint Committee joint entrance examination Klebsiella sp ladder polymers language means and SD message channel method metonymy Ministry of Education motion transmissibility National Chengchi University National Taiwan University Nomex Number of Students odd-numbered p-value PAN fibers passage G poem post-test pretest prevention costs PU/PSA polyblends quality cost information random walk reliability coefficient Research sample scores shrinkage stabilized fibers structure Study Table Taipei transmissibility ratio University National values Σ Σ 摘要