... PAN fibers affects the mechanical properties of the stabilized fibers and the final carbon fibers . In the stabilized fibers , a higher shrinkage of the PAN fibers during the stabilization process increased the oxygen content and the ...
... PAN fibers affects the mechanical properties of the stabilized fibers and the final carbon fibers . In the stabilized fibers , a higher shrinkage of the PAN fibers during the stabilization process increased the oxygen content and the ...
Seite 422
... fibers . The carbon fibers from sample B , C , and D appeared very porous . But , this finding needs to be confirmed ... PAN precursors developed with a fixed length method [ 24 ] . We have found that the tensile strength and modulus of the ...
... fibers . The carbon fibers from sample B , C , and D appeared very porous . But , this finding needs to be confirmed ... PAN precursors developed with a fixed length method [ 24 ] . We have found that the tensile strength and modulus of the ...
Seite 423
... fibers . Therefore , the tensile strengths of samples B and C are worse than of sample A , and that of sample D ... PAN fibers to shrink during the thermal stabilization . But , in manufacturing activated carbon fibers , the ...
... fibers . Therefore , the tensile strengths of samples B and C are worse than of sample A , and that of sample D ... PAN fibers to shrink during the thermal stabilization . But , in manufacturing activated carbon fibers , the ...
Andere Ausgaben - Alle anzeigen
Häufige Begriffe und Wortgruppen
academic departments access channels Admission to Higher Analysis appraisal costs bandwidth utilization base station blocking rate bolted joint C-test capture effect carbon fibers carbonization temperature Citrobacter cloze College Entrance Examination colleges and universities Committee on Admission defectives density Development distribution Enterobacter Entrance Examination Committee equation even-numbered Executive Yuan expected error External Failure Costs grid groups Herbert higher education Improvement increase institutions of higher Internal Failure Joint Committee joint entrance examination Klebsiella sp ladder polymers language M₁ means and SD message channel method metonymy Ministry of Education National Chengchi University National Taiwan University Nomex Number of Students odd-numbered p-value PAN fibers passage G poem post-test pretest prevention costs PU/PSA polyblends quality cost information random walk reliability coefficient Research sample scores shrinkage stabilized fibers structure Study Table Taipei transmissibility ratio University National values 摘要