... density of the nonwoven fabrics will increase as the density or depth of needle - punching are raise . Because the degree of binding forces of webs also increases the strength of nonwoven fabrics will be str- onger , but the air ...
... density of the nonwoven fabrics will increase as the density or depth of needle - punching are raise . Because the degree of binding forces of webs also increases the strength of nonwoven fabrics will be str- onger , but the air ...
Seite 416
... density gradient column method . The density column was prepared with a mixture of n - heptane and carbon tetrachloride so that a density gradient of about 1.2 to 1.6 g / cm3 extended from top to bottom . For the measurement of ...
... density gradient column method . The density column was prepared with a mixture of n - heptane and carbon tetrachloride so that a density gradient of about 1.2 to 1.6 g / cm3 extended from top to bottom . For the measurement of ...
Seite 421
... density versus carbonization temperature for the samples . Density increases very rapidly below the carbonization temperature of 1000 ° C for samples A and C and below 1100 ° C for samples B and D , respectively . But , above those ...
... density versus carbonization temperature for the samples . Density increases very rapidly below the carbonization temperature of 1000 ° C for samples A and C and below 1100 ° C for samples B and D , respectively . But , above those ...
Andere Ausgaben - Alle anzeigen
Häufige Begriffe und Wortgruppen
academic departments access channels Admission to Higher Analysis appraisal costs bandwidth utilization base station blocking rate bolted joint C-test capture effect carbon fibers Citrobacter cloze College Entrance Examination colleges and universities Committee on Admission defectives density Development distribution Enterobacter Entrance Examination Committee equation even-numbered Executive Yuan expected error External Failure Costs grid groups Herbert higher education Improvement increase institutions of higher Internal failure Joint Committee joint entrance examination Klebsiella sp ladder polymers language means and SD message channel method metonymy Ministry of Education motion transmissibility National Chengchi University National Taiwan University Nomex Number of Students odd-numbered p-value PAN fibers passage G poem post-test pretest prevention costs PU/PSA polyblends quality cost information random walk reliability coefficient Research sample scores shrinkage stabilized fibers structure Study Table Taipei transmissibility ratio University National values Σ Σ 摘要