... Densities of polyblends was listed in Fig.3 and Table III , respectiveily . In Fig.3 , the densities of the ... DENSITY ( g / cm3 ) 1.2 5 10 15. - 303- 聚氨基甲酸酯與聚( 4,4'-二苯磺醯基對苯醯胺)聚摻合體形態及機械性之研究 7 peared ...
... Densities of polyblends was listed in Fig.3 and Table III , respectiveily . In Fig.3 , the densities of the ... DENSITY ( g / cm3 ) 1.2 5 10 15. - 303- 聚氨基甲酸酯與聚( 4,4'-二苯磺醯基對苯醯胺)聚摻合體形態及機械性之研究 7 peared ...
Seite 416
... density gradient column method . The density column was prepared with a mixture of n - heptane and carbon tetrachloride so that a density gradient of about 1.2 to 1.6 g / cm3 extended from top to bottom . For the measurement of ...
... density gradient column method . The density column was prepared with a mixture of n - heptane and carbon tetrachloride so that a density gradient of about 1.2 to 1.6 g / cm3 extended from top to bottom . For the measurement of ...
Seite 421
... density versus carbonization temperature for the samples . Density increases very rapidly below the carbonization temperature of 1000 ° C for samples A and C and below 1100 ° C for samples B and D , respectively . But , above those ...
... density versus carbonization temperature for the samples . Density increases very rapidly below the carbonization temperature of 1000 ° C for samples A and C and below 1100 ° C for samples B and D , respectively . But , above those ...
Andere Ausgaben - Alle anzeigen
Häufige Begriffe und Wortgruppen
academic departments access channels Admission to Higher Analysis appraisal costs bandwidth utilization base station blocking rate bolted joint C-test capture effect carbon fibers carbonization temperature Citrobacter cloze College Entrance Examination colleges and universities Committee on Admission defectives density Development distribution Enterobacter Entrance Examination Committee equation even-numbered Executive Yuan expected error External Failure Costs grid groups Herbert higher education Improvement increase institutions of higher Internal Failure Joint Committee joint entrance examination Klebsiella sp ladder polymers language M₁ means and SD message channel method metonymy Ministry of Education National Chengchi University National Taiwan University Nomex Number of Students odd-numbered p-value PAN fibers passage G poem post-test pretest prevention costs PU/PSA polyblends quality cost information random walk reliability coefficient Research sample scores shrinkage stabilized fibers structure Study Table Taipei transmissibility ratio University National values 摘要