Seite 420
As shown in Table III , the carbon content of all samples increased with the increase in temperature during the carbonization stage . However , sample A has a greater carbon content than samples B , C , and D , indicating that the ...
As shown in Table III , the carbon content of all samples increased with the increase in temperature during the carbonization stage . However , sample A has a greater carbon content than samples B , C , and D , indicating that the ...
Seite 421
And , this misorientation of ladder polymers in stabilized fibers , such as samples B , C , and D , leads to poor orientation ... sample A decreased more slowly than the other samples which underwent a vapid linear decrease in density .
And , this misorientation of ladder polymers in stabilized fibers , such as samples B , C , and D , leads to poor orientation ... sample A decreased more slowly than the other samples which underwent a vapid linear decrease in density .
Seite 427
Diameter of carbon fibers as a function of carbonization temperature : O ) sample A ; ( o ) sample B ; ( + ) sample C ; ( A ) sample D. 78 Looo 76 74 72 A -- Preferred orientation ( % ) 70 ......... ..- A..k .
Diameter of carbon fibers as a function of carbonization temperature : O ) sample A ; ( o ) sample B ; ( + ) sample C ; ( A ) sample D. 78 Looo 76 74 72 A -- Preferred orientation ( % ) 70 ......... ..- A..k .
Was andere dazu sagen - Rezension schreiben
Es wurden keine Rezensionen gefunden.
Andere Ausgaben - Alle anzeigen
Häufige Begriffe und Wortgruppen
academic Accounting activities Admission to Higher Analysis applicants appraisal assume base better blocking Business C-test carbon fibers changes channel coefficient College Entrance Examination colleges and universities Committee continuous Decision decrease defectives density Department Design Development distribution effect equation error estimator expected failure costs Figure function given groups Herbert higher education Improvement increase indicates institutions International Joint Journal language Management materials means measured message channel method Ministry of Education obtained organization passage periodic Planning poem polymers practice prevention probability problem procedure properties quality costs random walk ratio reliability Report request Research respectively response sample schools scores selection shown shows shrinkage stabilization structure Study Subcommittee subjects suggestions Table Taiwan temperature transmissibility unit University values