... samples increased with the increase in temperature during the carbonization stage . However , sample A has a greater carbon content than samples B , C , and D , indicating that the misoriented ladder polymers in stabilized fibers will ...
... samples increased with the increase in temperature during the carbonization stage . However , sample A has a greater carbon content than samples B , C , and D , indicating that the misoriented ladder polymers in stabilized fibers will ...
Seite 421
... samples B , C , and D than in sample A. Because the ladder polymers in sample A were more nearly parallel to the fiber axis than the ladder polymer in the other samples , the broadening and lengthening of the polymers which occurs ...
... samples B , C , and D than in sample A. Because the ladder polymers in sample A were more nearly parallel to the fiber axis than the ladder polymer in the other samples , the broadening and lengthening of the polymers which occurs ...
Seite 427
... sample A ; ( O ) sample B ; ( + ) sample C ; ( △ ) sample D. Preferred orientation ( % ) 78 76 74 72 70 68 66 Δ 64 200 400 ལྟབ་ སྐ་ བ་ བ Δ Δ 600 800 1000 1200 Temperature ( ° C ) 1400 Figure 4. Preferred orientation of carbon fibers as ...
... sample A ; ( O ) sample B ; ( + ) sample C ; ( △ ) sample D. Preferred orientation ( % ) 78 76 74 72 70 68 66 Δ 64 200 400 ལྟབ་ སྐ་ བ་ བ Δ Δ 600 800 1000 1200 Temperature ( ° C ) 1400 Figure 4. Preferred orientation of carbon fibers as ...
Andere Ausgaben - Alle anzeigen
Häufige Begriffe und Wortgruppen
academic departments access channels Admission to Higher Analysis appraisal costs bandwidth utilization base station blocking rate bolted joint C-test capture effect carbon fibers carbonization temperature Citrobacter cloze College Entrance Examination colleges and universities Committee on Admission defectives density Development distribution Enterobacter Entrance Examination Committee equation even-numbered Executive Yuan expected error External Failure Costs grid groups Herbert higher education Improvement increase institutions of higher Internal Failure Joint Committee joint entrance examination Klebsiella sp ladder polymers language M₁ means and SD message channel method metonymy Ministry of Education National Chengchi University National Taiwan University Nomex Number of Students odd-numbered p-value PAN fibers passage G poem post-test pretest prevention costs PU/PSA polyblends quality cost information random walk reliability coefficient Research sample scores shrinkage stabilized fibers structure Study Table Taipei transmissibility ratio University National values 摘要