Seite 420
... samples increased with the increase in temperature during the carbonization stage . However , sample A has a greater carbon content than samples B , C , and D , indicating that the misoriented ladder polymers in stabilized fibers will ...
... samples increased with the increase in temperature during the carbonization stage . However , sample A has a greater carbon content than samples B , C , and D , indicating that the misoriented ladder polymers in stabilized fibers will ...
Seite 421
... samples B , C , and D than in sample A. Because the ladder polymers in sample A were more nearly parallel to the fiber axis than the ladder polymer in the other samples , the broadening and lengthening of the polymers which occurs ...
... samples B , C , and D than in sample A. Because the ladder polymers in sample A were more nearly parallel to the fiber axis than the ladder polymer in the other samples , the broadening and lengthening of the polymers which occurs ...
Seite 427
... sample A ; ( O ) sample B ; ( + ) sample C ; ( △ ) sample D. Preferred orientation ( % ) 78 100 76 74 Δ 72 A 70 68 66 64 200 400 600 800 1000 1200 1400 Temperature ( ° C ) Figure 4. Preferred orientation of carbon fibers as a function ...
... sample A ; ( O ) sample B ; ( + ) sample C ; ( △ ) sample D. Preferred orientation ( % ) 78 100 76 74 Δ 72 A 70 68 66 64 200 400 600 800 1000 1200 1400 Temperature ( ° C ) Figure 4. Preferred orientation of carbon fibers as a function ...
Andere Ausgaben - Alle anzeigen
Häufige Begriffe und Wortgruppen
academic departments access channels Admission to Higher Analysis appraisal costs bandwidth utilization base station blocking rate bolted joint C-test capture effect carbon fibers Citrobacter cloze College Entrance Examination colleges and universities Committee on Admission defectives density Development distribution Enterobacter Entrance Examination Committee equation even-numbered Executive Yuan expected error External Failure Costs grid groups Herbert higher education Improvement increase institutions of higher Internal failure Joint Committee joint entrance examination Klebsiella sp ladder polymers language means and SD message channel method metonymy Ministry of Education motion transmissibility National Chengchi University National Taiwan University Nomex Number of Students odd-numbered p-value PAN fibers passage G poem post-test pretest prevention costs PU/PSA polyblends quality cost information random walk reliability coefficient Research sample scores shrinkage stabilized fibers structure Study Table Taipei transmissibility ratio University National values Σ Σ 摘要