SEM was used to study the microstructures of some of the sintered disks . Other sintered disks were coated with Ag - paste , and fired at 350 ° C for 1 hr and 650 ° C for 2 hrs , immediately before the relative dielectric constant and ...
SEM was used to study the microstructures of some of the sintered disks . Other sintered disks were coated with Ag - paste , and fired at 350 ° C for 1 hr and 650 ° C for 2 hrs , immediately before the relative dielectric constant and ...
Seite 372
901 AXsr = 0.05 A Xsr : 0.10 80 : 0.15 sintering time = 2 hrs . Xer 701 Xsr : 0 Xsr = 0.05 Xsr = 0.10 % Theoretical density - 60 ... Effect of sintering temperature on the % theoretical density of sintered titanates . : 0 ( a ) Xer .
901 AXsr = 0.05 A Xsr : 0.10 80 : 0.15 sintering time = 2 hrs . Xer 701 Xsr : 0 Xsr = 0.05 Xsr = 0.10 % Theoretical density - 60 ... Effect of sintering temperature on the % theoretical density of sintered titanates . : 0 ( a ) Xer .
Seite 373
15KU89.97k 1.0M 681 - BAL a ) Xsr = 0.15 sintered at 1100 ° C x 2 hrs . 1.mum enal - BAL PAN 系碳纖維在碳化過程中物性. Fig . .7 . SEM micrographs of sintered titanate . 15KUX2.98K b ) Xsr = 0.10 sintered at 1300 ° C x 1 hr 1KU 89.9k ...
15KU89.97k 1.0M 681 - BAL a ) Xsr = 0.15 sintered at 1100 ° C x 2 hrs . 1.mum enal - BAL PAN 系碳纖維在碳化過程中物性. Fig . .7 . SEM micrographs of sintered titanate . 15KUX2.98K b ) Xsr = 0.10 sintered at 1300 ° C x 1 hr 1KU 89.9k ...
Was andere dazu sagen - Rezension schreiben
Es wurden keine Rezensionen gefunden.
Andere Ausgaben - Alle anzeigen
Häufige Begriffe und Wortgruppen
academic aged amount Analysis applied approach approximation assume autonomy become behavior bounded Chinese condition consider constant containing contingency decreasing defined denotes density distribution Economics effect equal equation establishes estimation expected exports field Figure finite element firm fixed follows foreign exchange market foreign exchange rate forward foreign exchange freedom function given gives Hence higher education importer-exporter imports increase independence institutions of higher integrations Journal Lemma less limits linear mean method needs normal observations obtain older parameters periodic populations positive probability problem procedure proof properties quantities random respect risk aversion rotor sample selection sell sintered social society solution solve standard statistic Step Study subset tables Taiwan temperature Theorem theory uncertainty University variables variance York zero