逢甲學報, Band 22逢甲大學, 1989 |
Im Buch
Ergebnisse 1-3 von 5
Seite 367
... sintering temperature and time . respectively . on the theoretical density of the sintered titanates . SEM micrographs of the titanates sintered at selected conditions are given in Fig . 7. As can be seen in this figure that better ...
... sintering temperature and time . respectively . on the theoretical density of the sintered titanates . SEM micrographs of the titanates sintered at selected conditions are given in Fig . 7. As can be seen in this figure that better ...
Seite 372
... sintering time = 2 hrs . 50L 1050 1250 1350 1150 Temperature ( ° C ) Fig . 5. Effect of sintering temperature on the % theoretical density of sintered titanates . 55 95 ( a ) 85 75 75 ( c ) ( b ) 65 ( a ) Xgr = 0.05 Xsr = 0.10 Xsr ...
... sintering time = 2 hrs . 50L 1050 1250 1350 1150 Temperature ( ° C ) Fig . 5. Effect of sintering temperature on the % theoretical density of sintered titanates . 55 95 ( a ) 85 75 75 ( c ) ( b ) 65 ( a ) Xgr = 0.05 Xsr = 0.10 Xsr ...
Seite 373
... sintered at 1100 ° C x 2 hrs . 15KU X9.98K 1.00UM 0001 -B & L b ) Xsr = 0.10 sintered at 1300 ° C x 1 hr 15KU X9.98K 1.00UM 0002 -B & L c ) xsr = 0.10 sintered at 1300 ° C x 2 hrs . Fig . 7. SEM micrographs of sintered titanate . PAN 系 ...
... sintered at 1100 ° C x 2 hrs . 15KU X9.98K 1.00UM 0001 -B & L b ) Xsr = 0.10 sintered at 1300 ° C x 1 hr 15KU X9.98K 1.00UM 0002 -B & L c ) xsr = 0.10 sintered at 1300 ° C x 2 hrs . Fig . 7. SEM micrographs of sintered titanate . PAN 系 ...
Andere Ausgaben - Alle anzeigen
Häufige Begriffe und Wortgruppen
A₁ A₂ absolute risk aversion algorithm amount of forward Analysis B₁ B₂ behavior best populations Chinese constant contingency tables coprecipitation Curie point decreasing absolute risk denotes density developmental tasks dielectric dielectric constant Dirichlet integrals establishes the forward EU"Z exchange rate Exponential finite element foreign exchange market foreign exchange rate forward foreign exchange function Goodness-of-Fit H₁ H₂ Hence higher education importer-exporter imports institutional autonomy institutions of higher integrations have limits Laplace transform Lemma linear obtain order statistics P(CS P(CSILFC P₁ percentile price uncertainty problem quantities of exports random variables risk aversion risk aversion effect rotor S₁ S₂ sample scale parameters selecting a subset Simonoff sinh sintered social society statistic stator Study t+At Taiwan temperature Theorem university autonomy V₁ vector Weibull distribution X₁ zero πο 摘要 第一期 第二期