... properties 3.1.1 Effect of spinning temperature on their physical properties The effect of spinning temperature from 293 ~ 299 ̊C to their mechanical properties was listed in Tables 1 and 2. As seen in Table 1 , it demonstrated that the ...
... properties 3.1.1 Effect of spinning temperature on their physical properties The effect of spinning temperature from 293 ~ 299 ̊C to their mechanical properties was listed in Tables 1 and 2. As seen in Table 1 , it demonstrated that the ...
Seite 378
... properties Sonic modulus | Boiling water ( % ) x E - 10 shrinkage ( ° C ) ( dyne / cm2 ) ( % ) 293 5.0 29.1 20.59 11.2 296 4.75 28.1 20.08 10.6 299 4.61 29.2 19.67 10.3 * all properties measured at fixed drawing temperature of 78 ° C ...
... properties Sonic modulus | Boiling water ( % ) x E - 10 shrinkage ( ° C ) ( dyne / cm2 ) ( % ) 293 5.0 29.1 20.59 11.2 296 4.75 28.1 20.08 10.6 299 4.61 29.2 19.67 10.3 * all properties measured at fixed drawing temperature of 78 ° C ...
Seite 379
... properties measured at fixed spinning temperature of 296 ° C and setting temperature of 120 ° C . 3.1.3 Effect of setting temperature on their physical properties The purpose of setting is to control the elongation and boiling water ...
... properties measured at fixed spinning temperature of 296 ° C and setting temperature of 120 ° C . 3.1.3 Effect of setting temperature on their physical properties The purpose of setting is to control the elongation and boiling water ...