The effect of spinning temperature on their physical properties Spinning temperature ( ° C ) Tenacity * ( g / d ) Elongation ( % ) Sonic modulus | Boiling water shrinkage ( % ) ( dyne / cm2 ) 20.59 11.2 x E - 10 293 5.0 29.1 296 4.75 ...
The effect of spinning temperature on their physical properties Spinning temperature ( ° C ) Tenacity * ( g / d ) Elongation ( % ) Sonic modulus | Boiling water shrinkage ( % ) ( dyne / cm2 ) 20.59 11.2 x E - 10 293 5.0 29.1 296 4.75 ...
Seite 379
The boiling water shrinkage was continuously decreased as the temperature raised . The effect of temperature on their birefringence was shown in Table 6 , it seemed to be irregular . Nevertheless the crystallinity and the density were ...
The boiling water shrinkage was continuously decreased as the temperature raised . The effect of temperature on their birefringence was shown in Table 6 , it seemed to be irregular . Nevertheless the crystallinity and the density were ...
Seite 383
... a mediumhigh degree correlation with the density , and a medium degree corelation with the elongation , the birefringence and the boiling water shrinkage , but a only a low degree correlation with the sonic modulus .
... a mediumhigh degree correlation with the density , and a medium degree corelation with the elongation , the birefringence and the boiling water shrinkage , but a only a low degree correlation with the sonic modulus .