Seite 378
The effect of spinning temperature on their physical properties Sonic modulus | Boiling water ( % ) x E - 10 shrinkage ( ° C ) ( dyne / cm2 ) ( % ) 293 5.0 29.1 20.59 11.2 296 4.75 28.1 20.08 10.6 299 4.61 29.2 19.67 10.3 * all ...
The effect of spinning temperature on their physical properties Sonic modulus | Boiling water ( % ) x E - 10 shrinkage ( ° C ) ( dyne / cm2 ) ( % ) 293 5.0 29.1 20.59 11.2 296 4.75 28.1 20.08 10.6 299 4.61 29.2 19.67 10.3 * all ...
Seite 379
The boiling water shrinkage was continuously decreased as the temperature raised . The effect of temperature on their birefringence was shown in Table 6 , it seemed to be irregular . Nevertheless the crystallinity and the density were ...
The boiling water shrinkage was continuously decreased as the temperature raised . The effect of temperature on their birefringence was shown in Table 6 , it seemed to be irregular . Nevertheless the crystallinity and the density were ...
Seite 383
... a medium- high degree correlation with the density , and a medium degree corelation with the elongation , the birefringence and the boiling water shrinkage , but a only a low degree correlation with the sonic modulus .
... a medium- high degree correlation with the density , and a medium degree corelation with the elongation , the birefringence and the boiling water shrinkage , but a only a low degree correlation with the sonic modulus .