Spinning temperature Tenacity * ( g / d ) Elongation Table 1. The effect of spinning temperature on their physical properties Sonic modulus | Boiling water ( % ) x E - 10 shrinkage ( ° C ) ( dyne / cm2 ) ( % ) 293 5.0 29.1 20.59 11.2 ...
Spinning temperature Tenacity * ( g / d ) Elongation Table 1. The effect of spinning temperature on their physical properties Sonic modulus | Boiling water ( % ) x E - 10 shrinkage ( ° C ) ( dyne / cm2 ) ( % ) 293 5.0 29.1 20.59 11.2 ...
Seite 379
The effect of drawing temperature on their structural and thermal properties Drawing temperature Birefringence * ( E - 3 ) Crystallinty ( % ) Density Melting point ( g / cm3 ) ( ° C ) ( ° C ) 73 0.2334 43.2 1.3744 255.9 78 0.2314 39.8 ...
The effect of drawing temperature on their structural and thermal properties Drawing temperature Birefringence * ( E - 3 ) Crystallinty ( % ) Density Melting point ( g / cm3 ) ( ° C ) ( ° C ) 73 0.2334 43.2 1.3744 255.9 78 0.2314 39.8 ...
Seite 382
3.2.2 Dynamic mechanical properties of yarn with different setting temperature The dynamic mechanical properties of spin - draw fiber was shown in Figure 4 at temperature of 110 ° C , 120 ° C , 125 ° C , 130 ° C . The maximum value of ...
3.2.2 Dynamic mechanical properties of yarn with different setting temperature The dynamic mechanical properties of spin - draw fiber was shown in Figure 4 at temperature of 110 ° C , 120 ° C , 125 ° C , 130 ° C . The maximum value of ...