Im Buch
Ergebnisse 1-3 von 28
Seite 378
The effect of spinning temperature on their physical properties Spinning temperature ( ° C ) Tenacity * ( g / d ) Elongation ( % ) Sonic modulus | Boiling water shrinkage ( % ) ( dyne / cm2 ) 20.59 11.2 x E - 10 293 5.0 29.1 296 4.75 ...
The effect of spinning temperature on their physical properties Spinning temperature ( ° C ) Tenacity * ( g / d ) Elongation ( % ) Sonic modulus | Boiling water shrinkage ( % ) ( dyne / cm2 ) 20.59 11.2 x E - 10 293 5.0 29.1 296 4.75 ...
Seite 379
The effect of drawing temperature on their structural and thermal properties Drawing temperature ( ° C ) Birefringence * Crystallinty ( E - 3 ) ( % ) Density ( g / cm3 ) Melting point ( ° C ) 73 0.2334 43.2 1.3744 255.9 78 0.2314 39.8 ...
The effect of drawing temperature on their structural and thermal properties Drawing temperature ( ° C ) Birefringence * Crystallinty ( E - 3 ) ( % ) Density ( g / cm3 ) Melting point ( ° C ) 73 0.2334 43.2 1.3744 255.9 78 0.2314 39.8 ...
Seite 382
3.2.2 Dynamic mechanical properties of yarn with different setting temperature The dynamic mechanical properties of spin - draw fiber was shown in Figure 4 at temperature of 110 ° C , 120 ° C , 125 ° C , 130 ° C . The maximum value of ...
3.2.2 Dynamic mechanical properties of yarn with different setting temperature The dynamic mechanical properties of spin - draw fiber was shown in Figure 4 at temperature of 110 ° C , 120 ° C , 125 ° C , 130 ° C . The maximum value of ...