... ( Figure 2 ) . The thermal behavior of the multi - block copolymers and their blends of nylon 6 with PSA was determined by DTA and TGA . Typical DTA curves and results for those block copolymers , the blends , as well as the homo ...
... ( Figure 2 ) . The thermal behavior of the multi - block copolymers and their blends of nylon 6 with PSA was determined by DTA and TGA . Typical DTA curves and results for those block copolymers , the blends , as well as the homo ...
Seite 377
... Figure 4 and Table 4. The slight increase of Tg indicated that the micro - Brownian motion of amorphous nylon 6 chains did suffer the restraint from the surrounding PSA molecules , especially the amounts of PSA were increased . But ...
... Figure 4 and Table 4. The slight increase of Tg indicated that the micro - Brownian motion of amorphous nylon 6 chains did suffer the restraint from the surrounding PSA molecules , especially the amounts of PSA were increased . But ...
Seite 380
... Figure 5 and Table 7 , it was shown that the nylon 6 / PSA blends had a higher crystalline temperature than that of the pure nylon 6. It indicated that the PSA molecules dispersed among the nylon 6 matrix could act as " nucleating ...
... Figure 5 and Table 7 , it was shown that the nylon 6 / PSA blends had a higher crystalline temperature than that of the pure nylon 6. It indicated that the PSA molecules dispersed among the nylon 6 matrix could act as " nucleating ...
Andere Ausgaben - Alle anzeigen
Häufige Begriffe und Wortgruppen
A₁ absolute risk aversion Analysis approximation autonomy B₁ b₂ C₁ carbon fiber characteristic equation China Chinese contingency tables copolyamides decision decreasing absolute risk defined denote developmental tasks Dirichlet distribution Dirichlet integrals Economic effect elasticity estimation fertility finite element foreign exchange market foreign exchange rate forward foreign exchange function H₁ H₂ Hence higher education importer-exporter income increase institutions of higher Insurance integral inverse k₁ k₂ ladder polymer Lemma linear Load Step matrix method normal distribution nylon obtain order statistics p-APA P(CS P₁ parameters polymer populations problem random variables risk aversion rotor S₁ S₂ sample selecting a subset sinh sintered solution stability statistic Study Table Taiwan temperature theorem Theory type-2 Dirichlet U₁ u₂ University V₁ variance Wang Weibull distribution X₁ Y₁ zero 摘要