... block copolymers were synthesized with a low molecular weight PSA prepolymer by chemical extending . Comparisons of the physical properties of these elastomers , it showed that both the polyblends and copolymers exhibited a glass ...
... block copolymers were synthesized with a low molecular weight PSA prepolymer by chemical extending . Comparisons of the physical properties of these elastomers , it showed that both the polyblends and copolymers exhibited a glass ...
Seite 347
... block copolymers of B1- B3 with polyblends of M5 , M10 and M15 ( the same amount of PSA ) in Table 2 and Figure 5 ... Block Copolymer The thermal properties of polyblends and block copolymers which were measured by DSC are shown in Table ...
... block copolymers of B1- B3 with polyblends of M5 , M10 and M15 ( the same amount of PSA ) in Table 2 and Figure 5 ... Block Copolymer The thermal properties of polyblends and block copolymers which were measured by DSC are shown in Table ...
Seite 354
... block copolymers as seen in Table 3 were found to be higher than those of polyblensd due to their better compatibility between PTMG and PSA segment . Consequently , we could prove later that the mechanical properties of the copolymers ...
... block copolymers as seen in Table 3 were found to be higher than those of polyblensd due to their better compatibility between PTMG and PSA segment . Consequently , we could prove later that the mechanical properties of the copolymers ...
Andere Ausgaben - Alle anzeigen
Häufige Begriffe und Wortgruppen
1-CV-GUTTER absorption approach Alexander Alexander's analysis anthraquinone anti-knowledge area of concentration b₁ balance of payments balance of trade block copolymers Brems College Curriculum Revision colleges and universities copolyamide PMA copolyamides courses currency curricula Curriculum Revision Committee curve Department of Higher devaluing country direct effects domestic dynamic programming effects of devaluation elasticities approach electron Engineering equation factorization property fluorene full employment function glass transition temperature higher education income effects increase individual academic departments initial institutions of higher Keynesian Lemma marginal propensity Marshall-Lerner condition maximal ideal Ministry of Education money income multiblock copolyamides Nylon output P₁ planned purchases polyblends Polym propensity to absorb R₁ reaction real income result Study supply synthesis Taiwan temperature terms of trade theorem Theory tion trade balance trade effect Tsiang TURB.K U₁ X₁ 摘要 摻合體及嵌狀共聚合體之製造及其物性之研究