Mechanics of Fretting FatigueSpringer Science & Business Media, 09.03.2013 - 246 Seiten Failures of many mechanical components in service result from fatigue. The cracks which grow may either originate from some pre-existing macroscopic defect, or, if the component is of high integrity but highly stressed, a region of localized stress concentration. In turn, such concentrators may be caused by some minute defect, such as a tiny inclusion, or inadvertent machining damage. Another source of surface damage which may exist between notionally 'bonded' components is associated with minute relative motion along the interface, brought about usually be cyclic tangential loading. Such fretting damage is quite insidious, and may lead to many kinds of problems such as wear, but it is its influence on the promotion of embryo cracks with which we are concerned here. When the presence of fretting is associated with decreased fatigue performance the effect is known as fretting fatigue. Fretting fatigue is a subject drawing equally on materials science and applied mechanics, but it is the intention in this book to concentrate attention entirely on the latter aspects, in a search for the quantification of the influence of fretting on both crack nucleation and propagation. There have been very few previous texts in this area, and the present volume seeks to cover five principal areas; (a) The modelling of contact problems including partial slip under tangentialloading, which produces the surface damage. (b) The modelling of short cracks by rigorous methods which deal effectively with steep stress gradients, kinking and closure. (c) The experimental simulation of fretting fatigue. |
Im Buch
Ergebnisse 1-5 von 47
Seite 2
... relative tangential displacement over at least part of the interface . Most frequently this condition occurs in ... relative displacements under radial load , and , after several millions of cycles of load , produced the damage depicted ...
... relative tangential displacement over at least part of the interface . Most frequently this condition occurs in ... relative displacements under radial load , and , after several millions of cycles of load , produced the damage depicted ...
Seite 3
... displacement , but with only a relatively small tangential force de- veloped . It is important to recognise that in any joint the area of contact may be composed of a complex pattern of slip regions , where relative tangential displacement ...
... displacement , but with only a relatively small tangential force de- veloped . It is important to recognise that in any joint the area of contact may be composed of a complex pattern of slip regions , where relative tangential displacement ...
Seite 4
... displacement fields , including implicitly the surface values , i.e. tractions and relative slip , is sufficient to quantify the process of crack initiation , early development and growth . The physical geometry of the contact will be ...
... displacement fields , including implicitly the surface values , i.e. tractions and relative slip , is sufficient to quantify the process of crack initiation , early development and growth . The physical geometry of the contact will be ...
Seite 5
... relative tangential displacement of the contacting pad has a profound influence on fretting performance : at low amplitudes the fretting influence is small . It increases with relative 1. INTRODUCTION 5.
... relative tangential displacement of the contacting pad has a profound influence on fretting performance : at low amplitudes the fretting influence is small . It increases with relative 1. INTRODUCTION 5.
Seite 6
... relative displacement up to some particular value , and then decreases at large amplitudes . It is usually accepted that the lack of effect at large displacements is because fretting wear is taking place , so that any embryo crack is ...
... relative displacement up to some particular value , and then decreases at large amplitudes . It is usually accepted that the lack of effect at large displacements is because fretting wear is taking place , so that any embryo crack is ...
Inhalt
5 | |
Contact of spheres the Hertz problem | 31 |
149 | 37 |
Contacts under Partial Slip | 41 |
Advanced Contact Mechanics | 65 |
9 | 101 |
26 | 108 |
41 | 115 |
60 | 149 |
1 | 169 |
Analysis of crack propagation | 175 |
Analysis of crack initiation | 199 |
Conclusions | 215 |
78 | 226 |
83 | 233 |
210 | 235 |
Andere Ausgaben - Alle anzeigen
Häufige Begriffe und Wortgruppen
applied arise asperity contact axi-symmetric behaviour bulk stress bulk tension Chapter coefficient of friction Comninou component compressive configuration constant contact patch contact problems contacting bodies crack faces crack initiation crack length crack propagation crack tip cyclic cylinders Dundurs effect elastically similar experimental Figure finite element finite element method fracture mechanics fretting fatigue fretting fatigue cracks fretting problems geometry given Green's functions half-plane hence Hertzian contact integral equation material Mech Mindlin mode normal load obtained occurs parameter partial slip plain fatigue plane plane strain plasticity possible predict region relative displacement relative slip residual stress shear force shear stress shear traction distribution shear tractions shown in fig singular sliding slip amplitude slip zones solution specimen spheres stick zone strain stress intensity factor surface displacements tangential displacement tangential force tangential loading technique tensile tests zero